CT285
日本京瓷
单组份,导热系数25W/mK,适合3-5W大功率LED和模组。自动点胶机适用。 1Introduction DieAttachPaste”KEMITITECT285”isepoxyresinbasedandsolventfreeTypepaste. Thehighestthermalconductivity(25W/mK) Goodreflowperformanceduelowermoistureabsorptionresinsystem. CT285iseffectivelyusedforpowerIC,transistor. 2Features 1)Goodworkabilityfordispensingduetosolventfreeandoneliquidtypepaste. 2)Highestthermalconductivity(25W/mK) 3)Bleedless. 3GeneralProperty Properties Unit TypicalValue TestMethod Appearance – SilverFilledPaste Visual Viscosityat25C Pa·s 100 EHDViscometer0.5rpm (3°cone) ThixotropicIndex – 6.0 0.5rpm/2.5rpm NonVoletile Wt% 92.0 180C×2hr SilverContent Wt% 87.5 600C×3hr AdhesiveStrength 25C 300C N 30 20 Frame:Cu/PPF ChipSize:2×2mm VolumeResistivity Ohm.cm 8×10-6 Cure:200C×90min Measurement:RoomTemp GlassTransitionTemperature C 200 TMA Modulus(25C) 25C GPa 16.5 DMA 260C 7.8 CTE Alpha1 Ppm 75 TMA Alpha2 200 IonicImpurity Na ppm 6 1 AtomicAbsorption Ionc